摘 要

有机发光二极管(Organic light emitting diode, OLED)在照明和先进显示器领域具有广阔的应用前景。与传统荧光材料相比,磷光有机金属材料因为在理论上能够达到百分百的内量子效率而受到广泛地关注。在其RGB三基色材料中,红色和蓝色磷光有机金属材料的研究已经取得了令人较为满意的成果,但绿磷光有机金属材料的色纯度、发光效率、热稳定性等方面还有改进的空间。目前,优良的具有稳定结构和合适的发光光谱的高效率磷光绿光材料分子主要是Ir配合物。与Ir配合物相比,在苯基咪唑卡宾配体与铂配合物环化合物方向,Pt配合物报道相对较少。然而Pt配合物显示出比已发表的Ir卡宾类似物更高的发光量子产率和更快的辐射衰变过程。与Ir配合物相比,Pt配合物的半峰宽较窄,而较窄的半峰宽有利于得到较纯的绿光材料,这引起了研究者极大的兴趣,大量的基于其的研究工作正在展开。本文设计制备了一种绿色磷光Pt配合物,并对其进行性质表征和性能测试,探究其光物理性质。

关键词:OLED;磷光材料;二价Pt配合物;绿光器件

Abstract

Organic light emitting diodes (OLEDs) have broad application prospects in the field of lighting and advanced displays. Compared with traditional fluorescent materials, phosphorescent organometallic materials are widely concerned because they can achieve 100% internal quantum efficiency in theory. Among its RGB three-color materials, the research of red and blue phosphorescent organometallic materials has achieved satisfactory results, but there is still room for improvement in color purity, luminescence efficiency, thermal stability and so on. At present, the high efficiency phosphorescent materials with stable structure and suitable luminescence spectrum are mainly Ir complexes. Compared with Ir complexes, Pt complexes have been rarely reported in the direction of phenyl imidazole carbene ligands with platinum complexes. nevertheless Pt complexes show higher luminescence quantum yields and faster radiative decay processes than published Ir carbene analogs. the half-peak width of Pt complexes is narrower than that of Ir complexes, and the narrow half-peak width is beneficial to obtain more pure green light materials, which has aroused great interest of researchers, and a lot of research work based on them is being carried out. In this article a green phosphorescence Pt based complex was designed and prepared, its properties of physical optics were characterized to explore its performance.

Keywords: Organic light emitting diode; Phosphorescent material; Platinum (II) complex; Green light Device

目 录

摘 要 I

Abstract II

第一章 文献综述 1

1.1 OLED简介 1

1.2 OLED材料发展历史 1

1.3 磷光OLED材料的研究现状 2

1.4本文研究内容 3

第二章 绿磷光材料Pt3的制备 3

2.1 实验内容 3

2.1.1 试剂和仪器 4

2.1.2 Pt3的合成 4

2.2 Pt3的表征 7

2.3 结果与讨论 10

第三章 Pt3的性能测试 11

3.1 前言 11

3.2 实验内容 11

3.2.1 紫外-可见吸收光谱测试 11

3.2.2 光致发光光谱测试 11

3.2.3 循环伏安曲线测试 12

3.3 结果与讨论 13

3.3.1 光谱总结 13

3.3.2 HOMO/LUMO能级计算 15

3.4 小结 15

第四章 结论与展望 16

4.1 结论 16

4.2 展望 16

参考文献 17

本科期间发表的学术论文 18

致 谢 19

附 录 20

第一章 文献综述

1.1 OLED简介

随着现代社会的发展,人类对于显示及照明的需求日益激增。在显示器件中,传统的CCFL、LED器件因其低功耗、可平板化、显示面积大等特点长期占有主要的市场份额。但同时它们也存在一系列的缺陷如亮度不均匀、可视角度小、相应时间长等。此外由于LCD器件的制造需要使用III- V族化学元素和一些重金属元素,使得生产和回收过程中极易造成对环境的破坏。

信息技术产业的发展,使得人们对显示设备的要求逐渐复杂,这也使得有机发光二极管(OLED)得到了充分的发展。基于其响应速度快、色域广、具有柔韧性等特点,OLED显示设备已经逐步占领市场。近几年,当下许多手机厂商的新机已广泛采用OLED材料制成的120HZ高刷新率屏幕、曲面屏幕,甚至可折叠屏等。这些都显示出OLED材料在照明和先进显示器领域具有广阔的应用前景。

1.2 OLED材料发展历史

剩余内容已隐藏,请支付后下载全文,论文总字数:20773字

您需要先支付 80元 才能查看全部内容!立即支付

该课题毕业论文、开题报告、外文翻译、程序设计、图纸设计等资料可联系客服协助查找;